余春林, 陈旭东, 宫川敏夫, 孙辉, 张兴旺, 童莉葛

Precursor with special structure for improving the performance of the ternary cathode material of Li-ion batteries

Chunlin YU, Xudong CHEN, Toshio MIYAGAWA, Hui SUN, Xingwang ZHANG, Lige TONG

表3 不同氨值条件下制备得到的正极材料与市售产品的主要理化指标

Table 3 Main physical and chemical indexes of cathode materials and commercial products prepared under different ammonia values

指标 NCM-L NCM-M NCM-H 市售产品 BET/(m2/g) 1.29 0.86 0.58 0.53 D50/μm 6.97 6.88 7.03 7.02 Li/% 1.03 1.03 1.03 1.02 Ni/% 0.827 0.828 0.825 0.825 Co/% 0.121 0.118 0.12 0.12 Mn/% 0.052 0.054 0.055 0.055 松装/(g/cm3) 1.64 1.72 1.79 1.77 H2O/10-6 586 562 514 534 自由Li+/% 1140 1433 1362 1450