铝离子电池电解液的研究进展

方亮, 张凯, 周丽敏

Recent advances and prospects of electrolyte for aluminum ion batteries

Liang FANG, Kai ZHANG, Limin ZHOU

图3 (a) 在电流密度100 mA/g，以AlCl3/尿素摩尔比1.3为电解液的AlII石墨电池在第20圈的充放电曲线；(b) 在电流密度变化后，保持100 mA/g的电流密度和2.2～1 V的电压窗口充放电至180圈的循环稳定性测试[18]；(c) 在电流密度100 mA/g，以AlCl3/尿素/[EMIm]Cl为电解液的AlIITPB电池250圈的长循环性能[19]；(d) 在电流密度100 mA/g，以MWCNT/S为正极和AlCl3/尿素为电解液的Al-S电池在不同圈数的充放电曲线[20]

Fig. 3 (a) Galvanostatic charge/discharge curve of AlIIgraphite cells using AlCl3/urea mole ratio 1.3 electrolyte at 20th cycle and 100 mA/g; (b) cycling stability test until 180 cycles at 100 mA/g within a voltage window of 2.2～1 V after current density changes[18]; (c) long cycling performance of AlIITPB battery with AlCl3/urea/[EMIm]Cl as electrolyte at 100 mA/g[19]; (d) charge/discharge curves of Al-S batteries with MWCNT/S cathode and AlCl3/urea electrolyte at 100 mA/g[20]