实用化复合锂负极研究进展
Recent advances in composite lithium anode under practical conditions
实用化复合锂负极研究进展 |
| 石鹏, 翟喜民, 杨贺捷, 赵辰孜, 闫崇, 别晓非, 姜涛, 张强 |
|
Recent advances in composite lithium anode under practical conditions |
| SHI Peng, ZHAI Ximin, YANG Hejie, ZHAO Chenzi, YAN Chong, BIE Xiaofei, JIANG Tao, ZHANG Qiang |
| 图2 (a) 软包电池中超薄锂在不同的电流密度和循环容量条件下的失效图，过渡区中圆形中不同颜色扇形面积比表示以极化和短路两种条件失效电池的比例；(b) 10.0 mA/cm2/10.0 mAh/cm2 循环10次之后，极片以及隔膜的光学及扫描电镜(SEM)图[ |
| Fig. 2 (a) Failure mechanism map at varied currents and capacities. The color of samples in the transition zone indicates the occurrence ratio of polarization and short-circuit failure; (b) The photo and scanning electron microscope (SEM) images of electrode and separator after 10 cycles at10.0 mA/cm2/10.0 mAh/cm2[ |
|
|