铬氧化物作为高容量锂电池正极材料的制备及其性能研究
Preparation and performance of high-capacity Cr8O21 as a cathode material for lithium batteries
铬氧化物作为高容量锂电池正极材料的制备及其性能研究 |
| 孟庆飞, 杨睿, 金成龙, 曹余良, 李文杰, 周舟, 吴际良 |
|
Preparation and performance of high-capacity Cr8O21 as a cathode material for lithium batteries |
| Qingfei MENG, Rui YANG, Chenglong JIN, Yuliang CAO, Wenjie LI, Zhou ZHOU, Jiliang WU |
| 图3 不同煅烧条件下所制备样品的SEM图。煅烧温度为(a) 250 ℃、(b) 270 ℃、(c) 290 ℃、(d) 300 ℃和(e) 360 ℃条件下煅烧12 h以及(f) 270 ℃条件下煅烧24 h |
| Fig. 3 SEM images of samples pyrolyzed at various temperatures (a) 250 ℃, (b) 270 ℃, (c) 290 ℃, (d) 300 ℃ and (e) 360 ℃ for 12 h and (f) pyrolysis at 270 ℃ for 12/24 h |
|
|