钠离子电池普鲁士蓝材料结构构建及优化的研究进展
陈娜, 李安琪, 郭子祥, 张钰哲, 秦学

Research progress on the construction and optimization of Prussian blue material structure for sodium-ion batteries
Na CHEN, Anqi LI, Zixiang GUO, Yuzhe ZHANG, Xue QIN
表1 钠离子电池普鲁士蓝正极材料的电化学性能
Table 1 Electrochemical performance of Prussian blue cathode materials for sodium-ion batteries
SamplesCapacity /(mAh/g@mA/g)Cyclability /(cycles, retention%@mA/g)Rate capacity /(mAh/g@mA/g)Refs.
Na1.41Mn0.32Fe0.11Co0.28Ni0.32Cu0.32[Fe(CN)6]·2.89H2O105@1550000,79@150036@7500[22]
K2Mn[Fe(CN)6]120@252000,75@10056@2000[24]
Na2Mn0.6Fe0.2Ni0.2(CN)6115@152000,66@75084@15000[25]
Na1.6Mn0.75(□Mn)0.25[Fe(CN)6]·1.57H2O137@252700,72@500100@500[30]
Na1.76FeFe(CN)6·2.6H2O115@201000,76@20075@4000[33]
Na2-xMnFe(CN)6164@10500,57@100110@500[35]
C‐FeHCF123@171000,87@170077.8@8500[38]
Na1.37Fe[Fe(CN)6]0.91⋅1.65 H2O130@503000,97@10000101@10000[39]
MnNiPB93@100500,96@10070@4000[58]