脂肪酸类二元储能材料的相变特性与配比调节
|
|
董金美, 刘启元, 吴芳, 贾利蕊, 文静, 常成功, 郑卫新, 肖学英
|
Phase change characteristics and proportion adjustment of fatty acid binary energy storage materials
|
|
Jinmei DONG, Qiyuan LIU, Fang WU, Lirui JIA, Jing WEN, Chenggong CHANG, Weixin ZHENG, Xueying XIAO
|
|
表5 二元复合体系低共熔配比附近DSC实测值与理论值的对比分析
|
Table 5 Comparison and analysis of DSC measured value and theoretical value near eutectic ratio of binary composite system
|
|
| 编号 | TTheo/℃ | TExpm/℃ | ΔT/% | HTheo/(J/g) | HExpm/(J/g) | ΔH/% |
|---|
| CA60-LA40 | 23.31 | 19.56 | -16.08 | 158.28 | 126.16 | -20.29 | | CA62-LA38 | 22.20 | 19.65 | -11.48 | 157.49 | 127.27 | -19.18 | | CA64-LA36 | 21.58 | 19.94 | -7.59 | 156.96 | 125.78 | -19.86 | | CA66-LA34 | 22.31 | 19.68 | -11.78 | 157.15 | 126.12 | -19.74 | | CA68-LA32 | 23.03 | 19.59 | -14.93 | 157.34 | 123.50 | -21.50 | | CA70-MA30 | 29.54 | 23.67 | -19.87 | 162.49 | 148.27 | -8.75 | | CA72-MA28 | 28.26 | 25.66 | -9.20 | 161.46 | 155.19 | -3.88 | | CA74-MA26 | 26.91 | 25.25 | -6.16 | 160.40 | 150.75 | -6.01 | | CA76-MA24 | 26.42 | 22.53 | -14.72 | 159.81 | 145.16 | -9.16 | | CA78-MA22 | 26.98 | 26.01 | -3.59 | 159.79 | 151.52 | -5.17 | | CA80-MA20 | 27.53 | 22.83 | -17.07 | 159.76 | 146.26 | -8.45 | | CA84-SA16 | 33.38 | 29.67 | -11.11 | 161.61 | 147.34 | -8.82 | | CA86-SA14 | 31.43 | 27.24 | -13.33 | 160.33 | 151.37 | -5.58 | | CA88-SA12 | 30.11 | 29.53 | -1.92 | 159.40 | 151.92 | -4.69 | | CA90-SA10 | 30.51 | 27.07 | -11.27 | 159.37 | 146.46 | -8.11 | | CA92-SA8 | 30.90 | 30.13 | -2.49 | 159.34 | 151.49 | -4.92 | | LA74-SA26 | 42.68 | 39.25 | -8.03 | 177.15 | 172.15 | -2.82 | | LA76-SA24 | 41.41 | 41.27 | -0.33 | 176.32 | 176.95 | 0.35 | | LA77-SA23 | 41.15 | 39.83 | -3.21 | 176.11 | 175.79 | -0.18 | | LA78-SA22 | 41.37 | 43.92 | 6.16 | 176.18 | 174.65 | -0.86 | | LA80-SA20 | 41.81 | 41.79 | -0.04 | 176.30 | 175.54 | -0.43 |
|
|
|