电解液浸泡对铝塑复合膜热封强度的影响

范  洋1，郭战胜1,2，冯捷敏2,3   

  1. 1上海市应用数学和力学研究所，上海 200072；2上海市力学在能源工程中的应用重点实验室，上海 200072；3上海大学理学院力学系，上海 200444
  • 收稿日期:2016-01-27 修回日期:2016-02-26 出版日期:2016-07-01 发布日期:2016-07-01
  • 通讯作者: 冯捷敏，主要从事锂电池系统和电极材料的电化学-力学耦合研究，E-mail：introrse@sina.com.cn。
  • 作者简介:范洋（1991—），男，硕士研究生，主要从事锂离子电池电极材料的力学性能研究，E-mail：865609392@qq.com
  • 基金资助:
    国家自然科学基金（11472165和11332005）。

Investigation on the influence of electrolyte on the heat-sealing strength of aluminum plastic composite foil

FAN Yang1, GUO Zhansheng 1,2, FENG Jiemin 2,3   

  1. 1Shanghai Institute of Applied Mathematics and Mechanics, Shanghai 200072, China; 2Shanghai Key Laboratory of Mechanics in Energy Engineering, Shanghai 200072, China; 3Department of Mechanics, College of Science, Shanghai University, Shanghai 200444, China
  • Received:2016-01-27 Revised:2016-02-26 Online:2016-07-01 Published:2016-07-01

PDF

968

被引次数

2

摘要：

铝塑复合膜作为软包装锂离子电池常用的封装材料，探究其热封强度的影响因素对于优化电池的安全性能很有意义。本工作通过实验测量铝塑膜在电解液浸泡下的热封强度，讨论两种浸泡方式（完整浸泡和局部浸泡）以及不同浸泡时间的影响。结果表明，完整浸泡后试样在不同热封工况（热封温度和热封时间）下的热封强度以及破坏模式基本一致，但是其热封强度不能完全反映热封区域的强度；局部浸泡使铝塑膜的尼龙层以及铝箔层在浸泡过程中避免电解液的影响，相对完整浸泡更能反映铝塑膜的热封强度，是比较合理的浸泡方式。浸泡后试样的热封强度随着浸泡时间的增加基本呈下降趋势，对于热封温度较低、热封时间较短的试样尤为明显，而对于热封温度较高、热封时间较长的试样影响较小。实验还发现浸泡过程中电解液的pH值逐渐降低，逐渐酸化的电解液对铝塑膜热封区域的腐蚀可能是其热封强度下降的原因之一。

关键词: 锂离子电池, 铝塑复合膜, 浸泡, 热封强度

Abstract:

 Aluminum plastic composite foil has become the common packaging material for soft package Li-ion battery, so it is worthy to study the influence factors of its heat-sealing strength to optimize safe capacity for battery. In this article, the heat-sealing strength of Al plastic foil after soaking in the electrolyte is tested by universal testing machine to discuss the influence of soaking ways(“soaking thoroughly” and “soaking partly”) and soaking time. It can be concluded that the heat-sealing strength and the failure modes under the different conditions(heat-sealing temperature and heat-sealing time) for “soaking thoroughly” is the same on basic, the achieved strength cannot reflect the real strength of heat-sealing zone. By contrast, the heat-sealing strength for soaking in bags can avoid the influence of the PA lay and the Al foil, so it is the better way to soak. In addition, the heat-sealing strength of Al plastic foil sinks after soaking, of which the trend is especially obvious for the specimens heat-sealed on lower heat-sealing temperature and shorter heat-sealing time. In experiments, it is found that during soaking the PH of electrolyte becomes lower, which may be one of the reasons for the sinking heat-sealing strength mentioned above.

Key words: Li-ion battery, aluminum plastic composite foil, soak, heat-sealing strength