PTCDI//δ-MnO2 水系铵离子电池性能研究

doi:10.19799/j.cnki.2095-4239.2021.0505

摘要/Abstract

摘要：

以铵根离子为载流子的可充电水系铵离子电池具有诸多本征优势，然而对于其全电池的研究与探索仍然处于起步阶段。本文首次报道了PTCDI//δ-MnO₂铵离子电池体系。该电池采用0.5 mol/L NH₄Ac作为电解液，以层状δ-MnO₂作为正极材料，3, 4, 9, 10-四甲酰二亚胺(PTCDI)作为有机负极，可以在0～1.5 V电压窗口内稳定工作。本文中的层状δ-MnO₂正极材料采用简单的KMnO₄热分解法制备，并通过XRD、SEM、TEM、XPS、FTIR、拉曼光谱等手段对δ-MnO₂纳米片正极进行了表征。实验研究结果表明，通过合理搭配PTCDI纳米粒子负极，该全电池在0.5 A/g的电流密度下循环500圈后，容量保持率仍为初始容量的92%，库仑效率接近100%，具有优异的循环稳定性。同时系统地研究了δ-MnO₂纳米片正极的储能机理以及PTCDI有机负极的储铵动力学特性。非原位XPS光谱结果表明NH₄⁺可以在正极材料中实现可逆地脱嵌。该全电池具有较高的电压窗口，可以较为轻松地向风扇及LED灯等常见小型电器供电，具有良好的发展前景。综上所述，新材料的开发对构建新一代安全环保的水系铵离子电池具有重要意义。

关键词: 水系铵离子电池, δ-MnO₂, PTCDI, 循环稳定性, 储铵机理

Abstract:

Rechargeable aqueous ammonium-ion batteries using ammonium ions as carriers have many inherent advantages; however, research and exploration of full batteries are still in their infancy. Herein, we developed a 3,4,9,10-perylenetetracarboxylic diimide (PTCDI)//δ-MnO₂ ammonium-ion battery system. The battery uses 0.5 mol/L NH₄Ac as the electrolyte, layered δ-MnO₂ as the cathode material, and PTCDI as the organic anode material, and it can work stably in the voltage range of 0—1.5 V. The layered δ-MnO₂ cathode material was prepared through simple thermal decomposition of KMnO₄ and was characterized by XRD, SEM, TEM, XPS, FTIR, and Raman spectroscopy. Through a proper combination of the PTCDI nanoparticle anode, the capacity retention rate of the full battery remained 92% of the initial capacity after 500 cycles at a current density of 0.5 A/g, and the coulombic efficiency was close to 100%, indicating excellent cycle stability. In addition, the energy storage mechanism of the δ-MnO₂ nanosheet cathode and the ammonium-ion storage dynamics kinetics of the PTCDI organic anode were systematically studied. Ex situ XPS revealed that NH₄⁺ can be reversibly intercalated/deintercalated in the cathode material. The full battery has a relatively high voltage window; thus, it can easily supply power to common electrical appliances, such as small fans and LEDs, and has a good development prospects. In summary, developing novel materials is of great significance to the construction of a new generation of safe and environmentally friendly aqueous ammonium-ion batteries.

Key words: aqueous ammonium-ion battery, δ-MnO₂, PTCDI, cycle stability, ammonium-ion storage mechanism

中图分类号:

O 646.21

孙颖, 赵钦, 尹博思, 马天翼. PTCDI//δ-MnO₂ 水系铵离子电池性能研究[J]. 储能科学与技术, 2022, 11(4): 1110-1120.

Ying SUN, Qin ZHAO, Bosi YIN, Tianyi MA. Performance of PTCDI//δ-MnO₂ aqueous ammonium-ion battery[J]. Energy Storage Science and Technology, 2022, 11(4): 1110-1120.

图/表 10

表1

图1

图2

图3

图4

图5

图6

图7

图8

图9

参考文献 42

1	GÜR T M. Review of electrical energy storage technologies, materials and systems: Challenges and prospects for large-scale grid storage[J]. Energy & Environmental Science, 2018, 11(10): 2696-2767.
2	LIU Y, SHI Y H, XU X H. Evolution and application of all-in-one electrochemical energy storage system[J]. Energy Storage Materials, 2021, 41: 677-696.
3	ZHOU G, XU L, HU G, et al. Nanowires for electrochemical energy storage[J]. Chemical Reviews, 2019, 119(20): 11042-11109.
4	LIU Z X, LI H F, ZHU M S, et al. Towards wearable electronic devices: A quasi-solid-state aqueous lithium-ion battery with outstanding stability, flexibility, safety and breathability[J]. Nano Energy, 2018, 44: 164-173.
5	ZHOU X, ZHAO A, CHEN Z X, et al. Research progress of tunnel-structural Na_0.44MnO₂ cathode for sodium-ion batteries: A mini review[J]. Electrochemistry Communications, 2021, 122: doi:10. 1016/j.elecom.2020.106897.
6	SCHMIDT A, RAMOS M K, FERREIRA C M, et al. Molybdenum-based materials/carbon nanotubes nanocomposites prepared as thin and transparent films for aqueous K-ion batteries[J]. Electrochimica Acta, 2021, 387: doi: 10.1016/j.electacta.2021.138500.
7	SHI Z Y, WU J H, NI M Z, et al. Superior performance of calcium birnessite by electrochemical conversion as cathode for aqueous calcium ion battery[J]. Materials Research Bulletin, 2021, 144: doi: 10.1016/j.materresbull.2021.111475.
8	ZHANG D L, CHEN Q, ZHANG J H, et al. MgMn₂O₄/multiwalled carbon nanotubes composite fabricated by electrochemical conversion as a high-performance cathode material for aqueous rechargeable magnesium ion battery[J]. Journal of Alloys and Compounds, 2021, 873: doi: 10.1016/j.jallcom.2021.159872.
9	衡永丽, 谷振一, 郭晋芝, 等. Na₃V₂(PO₄)₃@C用作水系锌离子电池正极材料的研究[J]. 储能科学与技术, 2021, 10(3): 938-944.
	HENG Y L, GU Z Y, GUO J Z, et al. Na₃V₂(PO₄)₃@C cathode material for aqueous zinc-ion batteries[J]. Energy Storage Science and Technology, 2021, 10(3): 938-944.
10	WANG D H, LV H, HUSSAIN T, et al. A manganese hexacyanoferrate framework with enlarged ion tunnels and two-species redox reaction for aqueous Al-ion batteries[J]. Nano Energy, 2021, 84: doi:10. 1016/j.nanoen.2021.105945.
11	WESSELLS C D, PEDDADA S V, MCDOWELL M T, et al. The effect of insertion species on nanostructured open framework hexacyanoferrate battery electrodes[J]. Journal of the Electrochemical Society, 2011, 159(2): A98-A103.
12	LI C Y, YAN W Q, LIANG S S, et al. Achieving a high-performance Prussian blue analogue cathode with an ultra-stable redox reaction for ammonium ion storage[J]. Nanoscale Horizons, 2019, 4(4): 991-998.
13	LI C Y, WU J H, MA F X, et al. High-rate and high-voltage aqueous rechargeable zinc ammonium hybrid battery from selective cation intercalation cathode[J]. ACS Applied Energy Materials, 2019, 2(10): 6984-6989.
14	WU X Y, XU Y K, JIANG H, et al. NH₄ ⁺ topotactic insertion in berlin green: An exceptionally long-cycling cathode in aqueous ammonium-ion batteries[J]. ACS Applied Energy Materials, 2018, 1(7): 3077-3083.
15	LUKATSKAYA M R, MASHTALIR O, REN C E, et al. Cation intercalation and high volumetric capacitance of two-dimensional titanium carbide[J]. Science, 2013, 341(6153): 1502-1505.
16	QIU S, XU Y K, LI X, et al. Reinforced potassium and ammonium storage of the polyimide anode in acetate-based water-in-salt electrolytes[J]. Electrochemistry Communications, 2021, 122: doi:10.1016/j.elecom.2020.106880.
17	ZHOU G Y, AN X Y, ZHOU C Y, et al. Highly porous electroactive polyimide-based nanofibrous composite anode for all-organic aqueous ammonium dual-ion batteries[J]. Composites Communications, 2020, 22: doi: 10.1016/j.coco.2020.100519.
18	KUCHENA S F, WANG Y. Superior polyaniline cathode material with enhanced capacity for ammonium ion storage[J]. ACS Applied Energy Materials, 2020, 3(12): 11690-11698.
19	HOLOUBEK J J, JIANG H, LEONARD D, et al. Amorphous titanic acid electrode: Its electrochemical storage of ammonium in a new water-in-salt electrolyte[J]. Chemical Communications (Cambridge, England), 2018, 54(70): 9805-9808.
20	DONG S Y, SHIN W, JIANG H, et al. Ultra-fast NH₄ ⁺ storage: Strong H bonding between NH₄ ⁺ and Bi-layered V₂O₅[J]. Chem, 2019, 5(6): 1537-1551.
21	LI H, YANG J, CHENG J L, et al. Flexible aqueous ammonium-ion full cell with high rate capability and long cycle life[J]. Nano Energy, 2020, 68: doi: 10.1016/j.nanoen.2019.104369.
22	KUMAR V, KUMAR V, WANG X, et al. Formation of hexagonal-molybdenum trioxide (h-MoO₃) nanostructures and their pseudocapacitive behavior[J]. Nanoscale, 2015, 7(27): 11777-11786.
23	CHAO D L, FAN H J. Intercalation pseudocapacitive behavior Powers aqueous batteries[J]. Chem, 2019, 5(6): 1359-1361.
24	KOMABA S, KUMAGAI N, CHIBA S. Synthesis of layered MnO₂ by calcination of KMnO₄ for rechargeable lithium battery cathode[J]. Electrochimica Acta, 2000, 46(1): 31-37.
25	WEI C G, XU C J, LI B H, et al. Preparation and characterization of manganese dioxides with nano-sized tunnel structures for zinc ion storage[J]. Journal of Physics and Chemistry of Solids, 2012, 73(12): 1487-1491.
26	XU J, LI J Q, YANG Q L, et al. In-situ synthesis of MnO₂@graphdiyne oxides nanocomposite with enhanced performance of supercapacitors[J]. Electrochimica Acta, 2017, 251: 672-680.
27	MA Z C, WEI X Y, XING S T, et al. Hydrothermal synthesis and characterization of surface-modified δ-MnO₂ with high fenton-like catalytic activity[J]. Catalysis Communications, 2015, 67: 68-71.
28	KAABI N, CHOUCHENE B, MABROUK W, et al. Electrochemical properties of a modified electrode with δ-MnO₂-based new nanocomposites[J]. Solid State Ionics, 2018, 325: 74-79.
29	SHAH H U, WANG F P, JAVED M S, et al. In-situ growth of MnO₂ nanorods forest on carbon textile as efficient electrode material for supercapacitors[J]. Journal of Energy Storage, 2018, 17: 318-326.
30	ZHAO Q, HUANG X J, ZHOU M M, et al. Proton insertion promoted a polyfurfural/MnO₂ nanocomposite cathode for a rechargeable aqueous Zn-MnO₂ battery[J]. ACS Applied Materials & Interfaces, 2020, 12(32): 36072-36081.
31	WANG D H, WANG L F, LIANG G J, et al. A superior δ-MnO₂ cathode and a self-healing Zn-δ-MnO₂ battery[J]. ACS Nano, 2019, 13(9): 10643-10652.
32	CHEN W, LI G D, PEI A, et al. A manganese-hydrogen battery with potential for grid-scale energy storage[J]. Nature Energy, 2018, 3(5): 428-435.
33	TANG Q W, JIANG L H, LIU J, et al. Effect of surface manganese valence of manganese oxides on the activity of the oxygen reduction reaction in alkaline media[J]. ACS Catalysis, 2014, 4(2): 457-463.
34	JUNTA J L, HOCHELLA M F Jr. Manganese (II) oxidation at mineral surfaces: A microscopic and spectroscopic study[J]. Geochimica et Cosmochimica Acta, 1994, 58(22): 4985-4999.
35	CHAO D, ZHU C, YANG P, et al. Array of nanosheets render ultrafast and high-capacity Na-ion storage by tunable pseudocapacitance[J]. Nature Communications, 2016, 7: doi: 10. 1038/ncomms12122.
36	WAN F, ZHANG L, DAI X, et al. Aqueous rechargeable zinc/sodium vanadate batteries with enhanced performance from simultaneous insertion of dual carriers[J]. Nat Commun, 2018, 9(1): 1656.
37	CHAO D, LIANG P, CHEN Z, et al. Pseudocapacitive Na-ion storage boosts high rate and areal capacity of self-branched 2D layered metal chalcogenide nanoarrays[J]. ACS Nano, 2016, 10(11): 10211-10219.
38	SONG Y, PAN Q, LV H, et al. Ammonium-ion storage using electrodeposited manganese oxides[J]. Angewandte Chemie (International Ed in English), 2021, 60(11): 5718-5722.
39	DELGADO M C, KIM E G, DA SILVA FILHO D A, et al. Tuning the charge-transport parameters of perylene diimide single crystals via end and/or core functionalization: A density functional theory investigation[J]. Journal of the American Chemical Society, 2010, 132(10): 3375-3387.
40	HAN X, CHANG C, YUAN L, et al. Aromatic carbonyl derivative polymers as high-performance Li-ion storage materials[J]. Advanced Materials, 2007, 19(12): 1616-1621.
41	DENG W, SHEN Y, QIAN J, et al. A perylene diimide crystal with high capacity and stable cyclability for Na-ion batteries[J]. ACS Applied Materials & Interfaces, 2015, 7(38): 21095-21099.
42	LESEL B K, KO J S, DUNN B, et al. Mesoporous LixMn₂O₄ thin film cathodes for lithium-ion pseudocapacitors[J]. ACS Nano, 2016, 10(8): 7572-7581.

[1]	徐钿昕, 田希坤, 闫君, 叶强, 赵长颖. TiO₂改性的CaCO₃热化学储热的反应性能[J]. 储能科学与技术, 2022, 11(1): 1-8.
[2]	Al-jawfi Ibrahim, 赵佳琦, 师萌, 康晓红. Al掺杂锰酸锂材料在水系锂离子电池中的循环稳定性[J]. 储能科学与技术, 2021, 10(4): 1330-1337.
[3]	陆贇, 梁嘉宁, 朱用, 李峥嵘, 胡冶州, 陈科, 王得丽. 有机物衍生的锂硫电池正极材料研究进展[J]. 储能科学与技术, 2020, 9(5): 1454-1466.
[4]	孟奇, 刘晓辉, 孙铭泽, 王其洋, 毕红. MXene/银纳米线超级电容器电极材料的电化学性能[J]. 储能科学与技术, 2019, 8(6): 1126-1131.
[5]	罗丽容, 蔡颖, 胡锋. 铸态及快淬态CeMg₁₁Ni合金电化学及其动力学性能[J]. 储能科学与技术, 2019, 8(5): 904-910.
[6]	房满庭, 章学来, 纪珺, 华维三, 刘彪, 王绪哲. 水合盐复合相变材料的研究进展[J]. 储能科学与技术, 2019, 8(4): 709-717.
[7]	刘家华, 徐晓英, 陈大柱, 洪娇玲, 孟潇, 欧阳星, 汤皎宁. 多孔CNTs@PANI修饰CNT纤维的制备及电化学性能[J]. 储能科学与技术, 2018, 7(6): 1226-1232.
[8]	周孙希, 章学来, 刘升. 十四烷-正辛酸有机复合相变材料的制备和性能[J]. 储能科学与技术, 2018, 7(4): 692-697.
[9]	李雨, 赵慧春, 白莹, 吴锋, 吴川. 高能量密度层状富锂锰基正极材料的改性研究进展[J]. 储能科学与技术, 2018, 7(3): 394-403.

PTCDI//δ-MnO₂ 水系铵离子电池性能研究

Performance of PTCDI//δ-MnO₂ aqueous ammonium-ion battery

RichHTML

PDF

可视化

摘要/Abstract

引用本文

使用本文

图/表 10

参考文献 42

相关文章 9

编辑推荐

Metrics

本文评价