基于火灾事故树模型的储能锂离子电池安全性检测方法与验证

doi:10.19799/j.cnki.2095-4239.2023.0039

摘要/Abstract

摘要：

规模化储能应用对锂离子电池提出了更高的安全性需求，充分挖掘储能用锂离子电池安全性检测技术对提升电池安全性能具有重要意义。GB/T 36276—2018《电力储能用锂离子电池》作为我国首个储能电池国家标准，其中规定的安全测试条款是否科学合理，检测方法是否可行亟待验证。本文基于储能锂电池安全事故触发因素，将火灾发生的必要因素通过火灾事故树原理层层分解。再利用布尔代数算法进行模拟，提出储能电池安全检测项目，与国家标准GB/T 36276—2018进行对比分析，验证了现行国家标准条款的科学合理性。最后基于试验平台，选用三元锂、钛酸锂、磷酸铁锂及锰酸锂等不同体系储能用锂离子电池开展了14种安全检测试验，对提出的测试项目进行试验验证。国内外首次验证了国家标准GB/T 36276—2018中安全测试条款的操作性和可行性，也为国家标准GB/T 36276新版本的修编提供了依据和数据支撑。

关键词: 储能, 锂离子电池, 安全, 检测, 标准

Abstract:

Large-scale energy storage applications require high safety measurements for lithium-ion batteries. Thus, the safety detection technology of lithium-ion batteries for energy storage should be fully explored to improve the safety performance of batteries. As the first national standard for energy storage batteries in China, GB/T 36276—2018 “Lithium ion battery for electrical energy storage" estimates whether the specified safety test provisions are scientific and reasonable and whether the test methods are feasible and need to be verified. First, based on the safety accident promotion factors of lithium batteries, this study decomposes the necessary fire factors via the fire accident tree principle. Then the Boolean algebraic algorithm is used to simulate and scientifically propose the safety detection items of energy storage batteries. The results are compared and analyzed with the national standard GB/T 36276—2018, which verifies the scientific rationality of the current national standard terms. Finally, based on the test platform, 14 safety testing experiments are performed on lithium-ion batteries for energy storage in different systems, such as lithium ternary, lithium titanate, lithium iron phosphate, and lithium manganate, to verify the proposed test items. The operability and feasibility of the safety test clauses in the national standard GB/T 36276—2018 have been verified for the first time at home and abroad, providing basis and data support for revising the new version of the national standard GB/T 36276.

Key words: energy storage, lithium ion battery, safety, testing, standard

中图分类号:

F 407.61

刘家亮, 郭翠静, 汪奂伶. 基于火灾事故树模型的储能锂离子电池安全性检测方法与验证[J]. 储能科学与技术, 2023, 12(5): 1695-1704.

Jialiang LIU, Cuijing GUO, Huanling WANG. Safety detection and verification of energy storage in lithium-ion battery based on fire fault tree model[J]. Energy Storage Science and Technology, 2023, 12(5): 1695-1704.

图/表 12

图1

图2

表1

表2

表3

表4

图3

图4

表5

表6

表7

表8

参考文献 19

1	黎冲, 王成辉, 王高, 等. 规模化储能技术发展分析与思考[J]. 电气时代, 2021(9): 22-28.
	LI C, WANG C H, WANG G, et al. Analysis and thinking on the development of large-scale energy storage technology[J]. Electric Age, 2021(9): 22-28.
2	郑帅, 鲁浩, 李文博, 等. 大规模储能在山东电力系统发展研究[J]. 电工技术, 2020(24): 35-37, 40.
	ZHENG S, LU H, LI W B, et al. Research on the development of large-scale energy storage in Shandong power system[J]. Electric Engineering, 2020(24): 35-37, 40.
3	李建林, 惠东, 靳文涛. 大规模储能技术[J]. 电气时代, 2018(12): 96.
	LI J L, HUI D, JIN W T. Large-scale energy storage technology[J]. Electric Age, 2018(12): 96.
4	孙秋娟, 冯丽华, 王青松, 等. 脉冲放电过程中锂离子电池的热行为分析[J]. 工程热物理学报, 2017, 38(9): 2038-2043.
	SUN Q J, FENG L H, WANG Q S, et al. The thermal response of lithium titanate battery during pulse discharge[J]. Journal of Engineering Thermophysics, 2017, 38(9): 2038-2043.
5	赵春朋, 王青松, 余彦. 密闭空间中锂离子电池的热爆炸危险性[J]. 储能科学与技术, 2018, 7(3): 424-430.
	ZHAO C P, WANG Q S, YU Y. Thermal explosion hazards of lithium-ion batteries in hermetic space[J]. Energy Storage Science and Technology, 2018, 7(3): 424-430.
6	谢潇怡, 王莉, 何向明, 等. 锂离子动力电池安全性问题影响因素[J]. 储能科学与技术, 2017, 6(1): 43-51.
	XIE X Y, WANG L, HE X M, et al. The safety influencing factors of lithium batteries[J]. Energy Storage Science and Technology, 2017, 6(1): 43-51.
7	黄沛丰, 刘家亮, 金翼, 等. 基于火三角模型的锂离子电池火灾事故树分析[J]. 安全与环境学报, 2018, 18(1): 66-69.
	HUANG P F, LIU J L, JIN Y, et al. Fault tree analysis method for lithium ion battery failure mode based on the fire triangle model[J]. Journal of Safety and Environment, 2018, 18(1): 66-69.
8	陈志斌, 王志远, 邵丹, 等. 动力锂离子电池安全性能检测标准化综述[J]. 电池, 2022, 52(6): 689-693.
	CHEN Z B, WANG Z Y, SHAO D, et al. Summary of standardization of safety performance testing for power lithium-ion batteries[J]. Battery Bimonthly, 2022, 52(6): 689-693.
9	王志远, 陈志斌, 邵丹, 等. 动力电池安全性能检测与评价标准体系框架构建[J]. 中国标准化, 2022(15): 62-66.
	WANG Z Y, CHEN Z B, SHAO D, et al. Construction of standard system framework for safety performance testing and evaluation of power batteries[J]. China Standardization, 2022(15): 62-66.
10	王彩娟, 宋杨, 秦剑峰, 等. 锂离子电池标准IEC 62619: 2017和GB/T 36276—2018解析[J]. 电池, 2020, 50(5): 483-487.
	WANG C J, SONG Y, QIN J F, et al. Analysis of the standards IEC 62619: 2017, GB/T 36276—2018 for Li-ion battery[J]. Battery Bimonthly, 2020, 50(5): 483-487.
11	EUNJI K, JUNHYEONG K, HO H S, et al. Detailed modeling investigation of thermal runaway pathways of a lithium iron phosphate battery[J]. International Journal of Energy Research, 2021, 46(2): 1146-1167.
12	HUANG P F, YAO C X, MAO B B, et al. The critical characteristics and transition process of lithium-ion battery thermal runaway[J]. Energy, 2020, 213: 119082.
13	LIU P J, LI Y Q, MAO B B, et al. Experimental study on thermal runaway and fire behaviors of large format lithium iron phosphate battery[J]. Applied Thermal Engineering, 2021, 192: 116949.
14	LIU P J, LIU C Q, YANG K, et al. Thermal runaway and fire behaviors of lithium iron phosphate battery induced by over heating[J]. Journal of Energy Storage, 2020, 31: doi: 10.1016/j.est.2020.101714.
15	胡洁, 方书昊, 齐涵, 等. 事故树-风险矩阵评估高校实验室火灾风险[J]. 安全, 2019, 40(5): 24-29.
	HU J, FANG S H, QI H, et al. Fire risk evaluation of the laboratory in colleges and universities based on fault tree analysis and risk matrix[J]. Safety & Security, 2019, 40(5): 24-29.
16	魏长旺. 基于事故树的电镀厂房火灾危险性分析[J]. 广东化工, 2021, 48(4): 250-251.
	WEI C W. Fire risk analysis of electroplating factory based on fault tree[J]. Guangdong Chemical Industry, 2021, 48(4): 250-251.
17	张霞, 朱杰. 基于事故树和模糊层次分析法的飞机火灾事故分析[J]. 安全, 2020, 41(4): 39-43.
	ZHANG X, ZHU J. Analysis on fire accident of airplane based on fault tree and fuzzy analytical hierarchy process[J]. Safety & Security, 2020, 41(4): 39-43.
18	许洁, 金静, 贾南, 等. 基于事故树与层次分析法的大型综合类商场火灾风险研究[J]. 武警学院学报, 2019, 35(8): 39-44.
	XU J, JIN J, JIA N, et al. Fire risk analysis on shopping complexes based on fault tree analysis and analytic hierarchy process[J]. Journal of the Armed Police Academy, 2019, 35(8): 39-44.
19	彭飞, 石娜丽. 基于事故树对某高校学生宿舍进行火灾隐患分析[J]. 吉林化工学院学报, 2019, 36(1): 43-47.
	PENG F, SHI N L. Analysis of fire hazard in A university dormitory based on fault tree analysis[J]. Journal of Jilin Institute of Chemical Technology, 2019, 36(1): 43-47.

基本事件组合	测试项目	测试对象	测试目的	仪器设备
x₁x₄x₇x₈x₁₂	过充电	储能电池单体、模块	模拟发生过充电的安全性	充放电设备
x₁x₄x₅x₆x₈x₁₂	过放电	储能电池单体、模块	模拟发生过放电的安全性	充放电设备
x₁x₄x₅x₆x₈x₁₅	短路	储能电池单体、模块	模拟发生短路时的安全性	短路试验测试系统
x₁x₄x₅x₆x₈x₁₁x₁₃x₁₄	挤压	储能电池单体、模块	模拟外力挤压时的安全性	挤压测试系统
x₁x₄x₅x₆x₈x₁₃x₁₄	震动	储能电池单体、模块	模拟不可抗拒因素或地质灾害等引起的安全性问题	震动测试系统
x₁x₄x₅x₆x₈x₁₁x₁₃x₁₄	冲击	储能电池单体、模块	模拟不可抗拒因素或地质灾害等引起的安全性问题	冲击测试系统
x₁x₄x₅x₆x₈x₁₁x₁₃x₁₄	跌落	储能电池单体、模块	模拟安装或维修时造成的自由跌落	跌落测试系统
x₁	低气压	储能电池模块	模拟在高空低气压运输或运行时的安全特性	低气压箱
x₁	盐雾	储能电池单体	模拟在海边高盐雾地区的使用情况	盐雾箱
x₁x₂x₃x₄x₅x₆x₈x₁₀x₁₅	热失控	储能电池单体	模拟电池单体发生热失控时的安全性	加速量热仪
x₁x₂x₃x₄x₅x₆x₈x₁₀x₁₅	热失控扩散	储能电池模块	模拟电池单体发生热失控时，触发电池模块系统内相邻或其他部位电池单体热失控的现象	加速量热仪
x₁x₂x₃x₄x₅x₆x₈x₁₀x₁₅	灼燃试验	储能电池单体	模拟外部缆线及其他零件燃烧对单体电池的影响	灼燃测试平台
x₁x₂x₃x₄x₅x₆x₈x₁₀x₁₅	火烧试验	储能电池模块	模拟泄漏电解液燃烧或其他电池热失控对上层电池安全性的影响	火烧试验系统

测试对象	测试项目	测试方法及要求
电池单体	过充电	充电至电压达到充电终止电压的1.5倍或时间达到1 h，不应起火、爆炸。
	过放电	放电至时间达到90 min或电压达到0 V，不应起火、爆炸。
	短路	正负极经外部短路10 min，不应起火、爆炸。
	挤压	挤压至电压达到0 V或变形量达到30%或挤压力达到(13±0.78) kN，不应起火、爆炸。
	跌落	正极或负极端子朝下从1.5 m高处自由跌落到水泥地面上1次，不应起火、爆炸。
	低气压	在低压环境中静置6 h，不应起火、爆炸、漏液。
	加热	以5 ℃的速率由环境温度升至(130±2) ℃并保持30 min，不应起火，爆炸。
	热失控	触发电池达到热失控的判定条件，不应起火、爆炸。
电池模块	过充电	充电至任一电池单体电压达到充电终止电压的1.5倍或时间达到1 h，不应起火、爆炸。
	过放电	放电至时间达到90 min或任一电池单体电压达到0 V，不应起火、爆炸。
	短路	正负极经外部短路10 min，不应起火、爆炸。
	挤压	挤压至变形量达到30%或挤压力达到(13±0.78) kN，不应起火、爆炸。
	跌落	正极或负极端子朝下从1.2 m高度处自由跌落到水泥地面上1次，不应起火、爆炸。
	盐雾与高温高湿	在海洋性气候条件下应满足盐雾性能要求，在喷雾-贮存循环条件下，不应起火、爆炸、漏液，外壳应无破裂现象；在非海洋性气候条件下应满足高温高湿性能要求，在高温高湿贮存条件下，不应起火、爆炸、漏液，外壳应无破裂现象。
	热失控扩散	特定位置的电池单体触发达到热失控的判定条件，不应起火、爆炸，不应发生热失控扩散。

电池编号	产品所属系别	电池类型	额定电压/V	额定容量/Ah	内阻/mΩ	充电终止电压/V	放电终止电压/V	质量/g
1#	磷酸铁锂	能量型	3.2	100	<1.0	3.65	2.50	2670
2#	磷酸铁锂	能量型	3.2	120	<1.0	3.65	2.50	2850
3#	钛酸锂	能量型	2.5	10	<1.2	2.7	1.5	287
4#	三元	能量型	3.7	26	<1.2	4.2	3.0	585
5#	锰酸锂	能量型	3.7	35	<1.2	4.2	2.7	810

样品编号	产品所属系别	电池类型	电池能量 /Wh	电池功率 /W	连接方式	额定电压 /V	额定容量 /Ah	充电终止电压 /V	放电终止电压 /V	外形尺寸 (长×宽×高)/mm
1#	磷酸铁锂	能量型	1920	860	5串1并	16	120	单体3.75	单体2.50	195×200×167
2#	磷酸铁锂	能量型	640	640	9串	26.4	50	单体3.75	单体2.50	440×85×54
3#	三元	功率型	38070	3807	—	141	271	单体4.20V	单体2.75	1200×1000×870
4#	三元	功率型	148	148	2并	3.7	40	单体4.20V	单体2.75	230×165×25
5#	磷酸铁锂	功率型	265	265	7串	23.1	11.5	单体3.65	单体2.50	192×63×47

编号	试验项目	样品种类	电池数量
1	过充	磷酸铁锂电池单体、三元电池单体	2 2
2	过放	磷酸铁锂电池单体	2
3	短路	磷酸铁锂电池单体及模块	各2
4	挤压	磷酸铁锂电池单体	2
5	针刺	锰酸锂电池单体三元电池模块	2 2
6	跌落	磷酸铁锂电池模块	2
7	振动	磷酸铁锂电池模块	2
8	盐雾	磷酸铁锂电池模块三元电池模块	2 2
9	高空低气压	磷酸铁锂电池单体	2
10	温度冲击	磷酸铁锂电池单体	2
11	绝热温升试验	磷酸铁锂电池单体	2
12	热失控	磷酸铁锂电池单体	2
13	热失控扩散	磷酸铁锂电池模块	2
14	灼燃	钛酸锂单体	2